Model number Composition
XOANONS®WE-D9540 Silicone modified hydroxyl acrylic resin
Specifications
|
Model number
|
Appearance
|
Solvent
|
Density
(g/ml)
(25±1)℃
|
Viscosity(mPa.s)
(25±0.2)℃
|
Content
(%)
(140℃ 2h）
|
Hydroxyl
(mgKOH/g to 100% solid portion)
|
|
XOANONS® WE-D9540
|
Slight yellowish
Tranparent liquid
|
BAC/
PMA
|
0.98-1.02
|
100-1000
(Rotary viscometer)
|
50±3
|
130
|
Application property and advantage
|
Model number
|
Property and advantage
|
|
XOANONS®
WE-D9540
|
Increase slip. Improve hydrophobicity and oleophobicity. Supply wipe-resistance from mark pen, and lotus effect. Better property of anti-graffiti and wipe-resistance from alcohol compared with anti-graffiti agent. Suit for surface of oven or other mental surface for oil/dirt proof and easy-cleaning requirement.
|
Construction specifications
1. Suggestion for PU formulation
|
|
Material
|
Dosage%
|
|
Part A
|
XOANONS®WE-D9540
|
50
|
|
Solvent
|
49.5
|
|
Dryer（1%）
|
0.5
|
|
Part B
|
N3390
|
12
|
Note：
1.N3390 is a cure agent from Bayer with a value of NCO%=19.6%.
2.The mixed part A and B should be used up within 5-7 hours in a sealed container. Otherwise, the mixed material will be gelled.
3.Suggest dry it at 80℃ for 1 hour or 150℃ for 5min.
2. Suggestion for baking system formulation
|
Material
|
Dosage
|
|
XOANONS®WE-D9540
|
50
|
|
Butylated amino resin
|
10
|
|
Solvent
|
38.5
|
|
Adhesion promoter
|
1
|
|
Acid catalyst
|
0.5
|
|
Total
|
100
|
Note：
1.The resin could be adjusted according to circumstance.
2.Suggest dry it at 150℃ for 30min or 210℃ for 90s.
Package
25KG 180KG
The container should be closed tightly before completely use up.
Storage
Should store in cool and dry place.
Can keep intact 24 months in original package.
|
Silicon leveling agnet